| Product | Cure Time | Shore A Hardness | Specific Gravity | Specific Volume | Color | Tensile Strength | Shrinkage | Elongation At Break | Hundred Percent Modulus | Die B Tear Strength | Useful Temperature Min | Mixed Viscocity | Mix Ratio By Volume | Mix Ratio By Weight | Pot Life | Hundred Percent Modulus | Color | Die B Tear Strength | Mixed Viscocity | Useful Temperature Min | Cure Time | Pot Life | Specific Volume | Specific Gravity | Mix Ratio By Weight | Shrinkage | Mix Ratio By Volume | Tensile Strength | Elongation At Break | Shore A Hardness | Dielectric Strength | Dielectric Strength |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Ecoflex™ 00 10 | 4 h. | 00-10 | 1.04 g/cc | 26.6 cu. in./lb. | Translucent | 120 psi | <.001 in. / in. | 800 % | 8 psi | 22 pli | -65 °F | 14,000 cps | 1A:1B | 1A:1B | 30 min. | 8 psi | Translucent | 22 pli | 14,000 cps | -65 °F | 4 h. | 30 min. | 26.6 cu. in./lb. | 1.04 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 120 psi | 800 % | 00-10 | - | - |
| Ecoflex™ 00 20 | 4 h. | 00-20 | 1.07 g/cc | 26.0 cu. in./lb. | Translucent | 160 psi | <.001 in. / in. | 845 % | 8 psi | 30 pli | -65 °F | 3,000 cps | 1A:1B | 1A:1B | 30 min. | 8 psi | Translucent | 30 pli | 3,000 cps | -65 °F | 4 h. | 30 min. | 26.0 cu. in./lb. | 1.07 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 160 psi | 845 % | 00-20 | - | - |
| Ecoflex™ 00 20 FAST | 1 h. | 00-20 | 1.07 g/cc | 26 cu. in./lb. | Translucent | 160 psi | <.001 in. / in. | 845 % | 8 psi | 30 pli | -65 °F | 3,000 cps | 1A:1B | 1A:1B | 20 min. | 8 psi | Translucent | 30 pli | 3,000 cps | -65 °F | 1 h. | 20 min. | 26 cu. in./lb. | 1.07 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 160 psi | 845 % | 00-20 | 350 volts/mil | 350 volts/mil |
| Ecoflex™ 00 30 | 4 h. | 00-30 | 1.07 g/cc | 26.0 cu. in./lb. | Translucent | 200 psi | <.001 in. / in. | 900 % | 10 psi | 38 pli | -65 °F | 3,000 cps | 1A:1B | 1A:1B | 45 min. | 10 psi | Translucent | 38 pli | 3,000 cps | -65 °F | 4 h. | 45 min. | 26.0 cu. in./lb. | 1.07 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 200 psi | 900 % | 00-30 | - | - |
| Ecoflex™ 00 50 | 3 h. | 00-50 | 1.07 g/cc | 25.9 cu. in./lb. | Translucent | 315 psi | <.001 in. / in. | 980 % | 12 psi | 50 pli | -65 °F | 8,000 cps | 1A:1B | 1A:1B | 18 min. | 12 psi | Translucent | 50 pli | 8,000 cps | -65 °F | 3 h. | 18 min. | 25.9 cu. in./lb. | 1.07 g/cc | 1A:1B | <.001 in. / in. | 1A:1B | 315 psi | 980 % | 00-50 | - | - |
Depuis plus de trente ans, nous recherchons dans le monde entier les matériaux de la plus haute qualité pour le modelage, le moulage et la coulée.
Des silicones et résines au Jesmonite et aux matériaux pour effets spéciaux — une gamme soigneusement sélectionnée pour les professionnels, artistes et créateurs.
Notre équipe commerciale est reconnue pour ses connaissances et son engagement, et vous accompagne dans le moulage, la coulée, la sculpture et le prototypage.
Nous expédions depuis nos entrepôts d'Amsterdam, Barcelone et Madrid vers des clients dans toute l'Europe, de la Grèce à la Norvège.
Fondée à Amsterdam, FormX est passée d'une fonderie d'art locale à un important fournisseur européen — avec nos racines fermement ancrées dans la ville.
FormX est spécialisé dans la fourniture et le commerce spécialisé de matériaux de modélisation 3D au sens le plus large du terme, et dispose d’entrepôts et de showrooms à Amsterdam, Barcelone et Madrid.